產(chǎn)品描述：

Sandstrom9A干膜潤滑劑是一種含有二硫化鉬和防腐蝕涂料的表面光澤涂層,這種熱固化涂層材料可以防止腐蝕、磨損,，它是一種的低摩擦系數(shù)的涂料，可以延長使用壽命，操作時超過-195°C到+ 260°C，耐負載100000 psi。
一旦Sandstrom9A熱固化以后，它不受大氣、摩擦腐蝕、溶劑、油、脫脂劑的影響。

Lubricative Pigment Molybdenum Disulfide

Color Flat Dark Gray
Shelf Life 1 year from date of Manufacture
Vacuum Outgassing None @ 10-6 Torr.
Lox Compatibility 100% compatible and shock resistant
Resistivity 1.4 x 106 OHMS CM
Coefficient of Friction 0.0236 (Falex Test)
Load Carrying Capacity 2250 lbs. ASTM D2625 B
Corrosion Protection OVER 1500 hours* ASTM B117
(@ .0005" DFT on DoD-P-16232 Type M
Class 3 phosphated steel)
*Test halted before failure occurred
COMPOSITION AND PHYSICAL PROPERTIES

9A should be applied where maximum wear life and corrosion
protection from a dry film lubricant are required.
once Sandstrom 9A has been heat cured, it is virtually
unaffected by atmospheric and fretting corrosion, solvents,
acids, oils, degreasers, and is not resoftened again at elevated
temperatures.
9A can be applied to a wide variety of surfaces by spraying
or dipping. Complete application instructions are on the
reverse of this sheet.
OUTSTANDING FEATURES/BENEFITS
Excellent Corrosion Protection, Chemical Resistance, and
Long Wear Life are its outstanding characteristics.
SANDSTROM 9A ConTAINS NO GRAPHITE
Use Sandstrom "099" as an alternative to 9A where low VOC
and no lead is preferred. 099's performance is comparable
to 9A.
TYPICAL USES
Sandstrom 9A is an excellent solution to the problem of lubricating
parts:
• That will be operated in corrosive atmospheres
• That may be stored for long periods
• Which are seldom lubricated once they leave the factory and
where permanent lubrication is desired
• Where operating pressures exceed the load-bearing capaci ties
of ordinary oils and greases
• Where "clean operation" is desired (9A will not collect dirt and
debris like grease and oils)
• Where a protective coating and sacrificial break-in lubricant
is needed
• Where fretting and galling is a problem (such as splines,
universal joints, and keyed bearings)
• Where easy release is desired (such as fasteners and PVC
molds)
• Where parts may be subjected to frequent disassembly